PENGKAJIAN MORTAR DAN PASTA GEOPOLIMER MATERIAL POZZOLAN SEBAGAI SUPPLEMENTARY CEMENTITIOUS MATERIALS (SCMS) DARI LIMBAH POTENSI AGRO DAN INDUSTRI DI INDONESIA

GEOPOLIMER MERUPAKAN PEMBAHARUAN MATERIAL KONSTRUKSI RAMAH LINGKUNGAN YANG DAPAT MENGURANGI DAMPAK BURUK DARI MANUFAKTUR SEMEN KONVENSIONAL. PARAMETER UTAMA PADA PENGKAJIAN GEOPOLIMER ADALAH MATERIAL POZZOLAN YANG DIGUNAKAN SEBAGAIBAHAN PENGIKAT PENGGANTI SEMEN DENGAN KANDUNGAN ALUMINOSILICATE (SIAL) TINGGI. DI INDONESIA, MATERIAL POZZOLAN MEMILIKI POTENSI MELIMPAH TERUTAMA PADA LIMBAH INDUSTRI DAN AGRIKULTUR SEPERTI ABU TERBANG BATU BARA, LIMBAH KACA, SEKAM PADI, AMPASTEBU, DAN CANGKANG SAWIT APABILA DIOLAH MENJADI POWDER. OLEH SEBAB ITU, PENELITIAN INIMENGKAJI BERBAGAI POTENSI MATERIAL POZZOLAN DARI LIMBAH INDUSTRI DAN AGRIKULTUR DI INDONESIA MENGGUNAKAN 5 VARIASI KOMBINASI BERUPA FA100%, FA95%+AAT5%, FA90%+ASP10%, FA90%+ACS10%, DAN FA90%+BK10 DENGAN PENAMBAHAN NAOH/NA2SIO3 SEBESAR 1:2,5 YANG DILAKUKAN PERAWATAN SELAMA 28 HARI. PENELITIAN INI JUGA MENAMBAHKAN SUPERPLASTICIZER 2 DENGAN PENAMBAHAN NAOH/NA2SIO3 SEBESAR 1:2,5 YANG DILAKUKAN PERAWATAN SELAMA 28 HARI. PENELITIAN INI JUGA MENAMBAHKAN SUPERPLASTICIZER 2 DAN AQUADEST 10% UNTUK MENINGKATKAN WORKABILITY PADA GEOPOLIMER. PENGUJIAN YANG DILAKUKAN BERUPA UJI SETTING TIME PASTA, FLOWABILITY, DAN KUAT TEKAN MORTAR GEOPOLIMER. PENGUJIAN SETTING TIME DIPEROLEH HASIL BERUPA WAKTU PENGIKATAN AWAL RENTANG 25-75 MENIT DAN WAKTU PENGIKATAN AKHIR 40- 115 MENIT. PENGUJIAN FLOWABILITY DIPEROLEH NILAI 180-250 MM DAN PENGUJIAN KUAT TEKAN DIPEROLEH NILAI 25-36 MPA. BERDASARKAN PENGUJIAN SETTING TIME, DISIMPULKAN BAHWA WAKTU PENGIKATAN TERCEPAT TERJADI PADA FA95%+AAT5%, YAITU 40 MENIT KARENA KANDUNGAN CAO DAN SIO2 CUKUP TINGGI. PADA PENGUJIAN FLOWABILITY, FA100% MEMILIKINILAI DIAMETER FLOW PALING TINGGI, YAITU 250 MM KARENA BERAT JENIS MATERIAL TERSEBUT PALING BESAR. SELANJUTNYA, PENGUJIAN KUAT TEKAN DIPEROLEH NILAI KUAT TEKAN TERTINGGI PADA FA90%+ASP10% SEBESAR 36,36 MPA KARENA KANDUNGAN SIO2 MATERIAL TERSEBUT PALING TINGGI. SELURUH HASIL KUAT TEKAN MEMPEROLEH NILAI >20 MPA SEHINGGA DAPAT DIAPLIKASIKAN DALAM KONSTRUKSI STRUKTURAL SEPERTI GEDUNG DAN JEMBATAN