KARAKTERISASI SIFAT KETANGGUHAN IMPAK DAN TERMAL KOMPOSIT HIBRID ABAKA/KARBON/EPOXY

KOMPOSIT SERAT ALAM MERUPAKAN MATERIAL YANG POTENSIAL UNTUK DIKEMBANGKAN DAN DIGUNAKAN DALAM BERBAGAI BIDANG, SALAH SATUNYA YAITU DALAM BIDANG BIOMEDIS UNTUK MEMBUAT PERANGKAT SEPERTI SOCKET PROSTHESIS. SERAT ALAM MEMILIKI SIFAT YANG RAMAH LINGKUNGAN, BIODEGARDABLE, DAN LEBIH EKONOMIS. PADA SAAT INI, SEBAGIAN BESAR SOCKET PROSTHESIS MASIH MENGGUNAKAN KOMPOSIT POLIMER BERPENGUAT SERAT SINTETIS YANG MEMILIKI SIFAT TIDAK EKONOMIS, TIDAK BAIK UNTUK KESEHATAN DAN TIDAK RAMAH LINGKUNGAN. AKAN TETAPI, KOMPOSIT POLIMER BERPENGUAT SERAT ALAM SEBAGAI BAHAN ALTERNATIF SOCKET PROSTHESIS JUGA MEMILIKI KELEMAHAN YAITU SIFAT MEKANIS YANG BERVARIASI, TERGANTUNG DARI FAKTOR YANG MEMPENGARUHINYA. UNTUK MENGATASI HAL TERSEBUT, KOMPOSIT SERAT ALAM DAPAT DIHIBRIDISASI UNTUK MENINGKATKAN SIFAT MEKANISNYA. PENELITIAN INI BERTUJUAN UNTUK MENGETAHUI KETANGGUHAN IMPACT KOMPOSIT ABAKA/KARBON/EPOXY DENGAN VARIASI SERAT ABAKA DAN SERAT KARBON 2:1, 3:1, DAN 4:1 SERTA MENGETAHUI SIFAT TERMAL KOMPOSIT TERSEBUT.
PENELITIAN INI MENGGUNAKAN SERAT ABAKA DAN KARBON UNTUK MEMPERKUAT RESIN EPOXY DENGAN PANJANG MASING-MASING 4 MM DAN 6 MM. FRAKSI VOLUME YANG DIGUNAKAN 80% MATRIKS : 20% PENGUAT. KOMPOSIT DIBUAT DENGAN METODE HAND LAY-UP DAN HOT PRESS MOULDING. SEBELUM FABRIKASI KOMPOSIT, SERAT ABAKA DIPERLAKUKAN DENGAN ALKALISASI NAOH 6% SELAMA 36 JAM, DAN SERAT KARBON DIPERLAKUKAN DENGAN PERENDAMAN DALAM NITROGEN CAIR SELAMA 10 MENIT. UJI IMPAK DAN TERMOGRAVIMETRI DILAKUKAN MENGIKUTI ASTM D6110 DAN ASTM E1131. STRUKTUR MIKRO PADA PERMUKAAN PATAHAN UJI IMPAK DILIHAT MELALUI SCANNING ELECTRON MICROSCOPE (SEM).

HASIL PENELITIAN MENUNJUKKAN BAHWA PERLAKUAN SERAT KARBON MENINGKATKAN KEKUATAN IMPAK KOMPOSIT KARBON/EPOXY. NAMUN, PERLAKUAN ALKALI SERAT ABAKA MENURUNKAN KEKUATAN IMPAK KOMPOSIT ABAKA/EPOXY. KEKUATAN IMPAK KOMPOSIT HYBRID ABAKA/KARBON/EPOXY DENGAN RASIO SERAT ABAKA/KARBON 2:1, 3:1, DAN 4:1 TIDAK BERBEDA SECARA SIGNIFIKAN DENGAN KOMPOSIT ABAKA/EPOXY. BERDASARKAN HASIL ANALISIS TERMOGRAVIMETRI, KOMBINASI SERAT ABAKA DAN SERAT KARBON DAPAT MENAHAN STABILITAS TERMAL KOMPOSIT HYBRID ABAKA/KARBON/EPOXY.