PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP SIFAT MEKANIS DENGAN LOW SPEED TENSILE TEST CAMPURAN POLYPROPYLENE - ACRYLONITRILE BUTADIENE STYRENE

MOHAMMAD FAHREZA IKHSAN (2022) PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP SIFAT MEKANIS DENGAN LOW SPEED TENSILE TEST CAMPURAN POLYPROPYLENE - ACRYLONITRILE BUTADIENE STYRENE. S1 thesis, Universitas Muhammadiyah Yogyakarta.

[thumbnail of Halaman Judul] Text (Halaman Judul)
Halaman Judul.pdf

Download (692kB)
[thumbnail of Lembar Pengesahan] Text (Lembar Pengesahan)
Lembar Pengesahan.pdf
Restricted to Registered users only

Download (429kB)
[thumbnail of Abstrak] Text (Abstrak)
Abstrak.pdf
Restricted to Registered users only

Download (100kB)
[thumbnail of Bab I] Text (Bab I)
Bab I.pdf

Download (110kB)
[thumbnail of Bab II] Text (Bab II)
Bab II.pdf
Restricted to Registered users only

Download (719kB)
[thumbnail of Bab III] Text (Bab III)
Bab III.pdf
Restricted to Registered users only

Download (606kB)
[thumbnail of Bab IV] Text (Bab IV)
Bab IV.pdf
Restricted to Registered users only

Download (462kB)
[thumbnail of Bab V] Text (Bab V)
Bab V.pdf
Restricted to Registered users only

Download (97kB)
[thumbnail of Daftar Pustaka] Text (Daftar Pustaka)
Daftar Pustaka.pdf
Restricted to Registered users only

Download (175kB)
[thumbnail of Lampiran] Text (Lampiran)
Lampiran.pdf
Restricted to Registered users only

Download (2MB)
[thumbnail of Naskah Publikasi] Text (Naskah Publikasi)
Naskah Publikasi.pdf
Restricted to Registered users only

Download (296kB)
[thumbnail of Full Text] Text (Full Text)
Full Text.pdf
Restricted to Repository staff only

Download (5MB)

Abstract

CAMPURAN POLIMER MENJADI SALAH SATU METODE YANG EFEKTIF DALAM PENGEMBANGAN INDUSTRI POLIMER. PENERAPAN TEKNIK INI DAPAT MENCIPTAKAN BAHAN BARU DENGAN KINERJA DAN SIFAT YANG BARU. POLYPROPYLENE (PP) DAN ACRYLONITRILE BUTADIENE STYRENE (ABS) ADALAH POLIMER KOMODITAS YANG PALING BANYAK DIGUNAKAN KARENA SIFAT MEKANIKNYA YANG BAIK. PENELITIAN PP DAN ABS DENGAN MENGGUNAKAN MESIN EKSTRUSI MASIH BELUM BANYAK. PENELITIAN INI BERTUJUAN UNTUK MENGETAHUI PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP PENGUJIAN TARIK DAN STRUKTUR MORFOLOGI CAMPURAN PP DAN ABS.

PENELITIAN DILAKUKAN DENGAN MEMBUAT SPESIMEN SESUAI STANDAR ASTM D 638 DARI BAHAN BUTIRAN PP DAN ABS. CAMPURAN PP DAN ABS DILAKUKAN DENGAN MENGGUNAKAN MESIN EKSTRUSI. METODE BLENDED DILAKUKAN DENGAN RATIO PP 40% : ABS 60%, PP 50% : ABS 50%, PP 60% : ABS 40%. PENGUJIAN SPESIMEN YANG DILAKUKAN YAITU UJI TARIK DAN FOTO MIKRO.

HASIL PENGUJIAN TARIK MENUNJUKKAN BAHWA KEKUATAN TERTINGGI (42,5 MPA) DAN MODULUS (264 MPA) PADA PERBANDINGAN 50% PP : 50

Item Type: Thesis (S1)
Uncontrolled Keywords: BLENDING RATIO, MELTING TEMPERATURE, POLYPROPYLENE, ACRYLONITRILE BUTADIENE STYRENE, PENGUJIAN TARIK BLENDING RATIO, MELTING TEMPERATURE, POLYPROPYLENE, ACRYLONITRILE BUTADIENE STYRENE, TENSILE TEST
Divisions: Fakultas Teknik > Teknik Mesin S1
Depositing User: M. Erdiansyah
Date Deposited: 20 Apr 2022 03:04
Last Modified: 20 Apr 2022 03:04
URI: https://etd.umy.ac.id/id/eprint/29498

Actions (login required)

View Item
View Item