PENCEGAHAN KOROSI DENGAN METODE STEEL COATING DAN CONCRETE SURFACE COATING PADA TAP WATER MIXED MORTAR DENGAN BAHAN IKAT PORTLAND COMPOSITE CEMENT (PCC)

BETON MERUPAKAN MATERIAL YANG MEMILIKI BANYAK FUNGSI SEHINGGA BANYAK DIGUNAKAN DALAM DUNIA KONSTRUKSI. BETON BERTULANG DAPAT MENGALAMI PENURUNANA DAYA TAHAN STRUKTUR YANG DISEBABKAN OLEH KOROSI. KOROSI TERJADI AKIBAT KONDISI LINGKUNGAN YANG MEMILIKI UAP AIR YANG TINGGGI DAN JUGA PERUBAHAN UDARA YANG EKSTRIM SERTA LINGKUNGAN LAUT SEHINGGA PENCEGAHAN KOROSI SANGAT DIPERLUKAN UNTUK MEMPERLAMBAT POTENSI KOROSI PADA TULANGAN BAJA DIDALAM BETON. PENCEGAHAN KOROSI YANG DILAKUKAN PADA PENELITIAN INI MENGGUNAKAN METODE COATING DAN PENEBALAN SELIMUT BETON. METODE COATING YANG DIGUNAKAN YAITU STEEL COATING DAN CONCRETE SURFACE COATING, KEMUDIAN UNTUK METODE PENEBALAN SELIMUT BETON DIGUNAKAN SELIMUT BETON BERUKURAN 3 CM DAN 10 CM. SIMULASI LINGKUNGAN KOROSIF DILAKUKAN MENGGUNAKAN EXPOSURE CONDITION DRY-WET CYCLE, WET CONRITION DAN DRY LABORATORY CONDITION. PENGAMATAN KOROSI MENGGUNAKAN METODE PENGUJIAN HALF-CELL POTENTIAL BERLANGSUNG SELAMA 56 HARI UNTUK MENGETAHUI NILAI POTENSI KOROSI YANG TERJADI PADA SETIAP SPESIMEN. HASIL PENGUJIAN MENUNJUKKAN NILAI POTENSI KOROSI PADA BENDA UJI DENGAN METODE CONCRETE SURFACE COATING DAN STEEL COATING MEMBERIKAN NILAI POTENSI KOROSI LEBIH POSITIF DIBANDINGKAN DENGAN SPESIMEN NON COATING, SERTA SPESIMEN DENGAN KETEBALAN SELIMUT 10 CM MEMBERIKAN NILAI POTENSI KOROSI YANG LEBIH POSITIF DIBANDINGKAN DENGAN SPESIMEN DENGAN KETEBALAN SELIMUT 3 CM SEHINGGA DAPAT DISIMPULKAN METODE COATING DAN PENAMBAHAN TEBAL SELIMUT BETON DAPAT MENJADI SOLUSI KASUS KOROSI BETON BERTULANG