PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP LOW SPEED TENSILE TEST CAMPURAN POLYPROPYLENE MURNI-DAUR ULANG

ARIEF PRIHANDOKO (2022) PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP LOW SPEED TENSILE TEST CAMPURAN POLYPROPYLENE MURNI-DAUR ULANG. S1 thesis, Universitas Muhammadiyah Yogyakarta.

[thumbnail of Halaman Judul] Text (Halaman Judul)
Halaman Judul.pdf

Download (398kB)
[thumbnail of Lembar Pengesahan] Text (Lembar Pengesahan)
Lembar Pengesahan.pdf
Restricted to Registered users only

Download (317kB)
[thumbnail of Abstrak] Text (Abstrak)
Abstrak.pdf
Restricted to Registered users only

Download (55kB)
[thumbnail of Bab I] Text (Bab I)
Bab I.pdf

Download (64kB)
[thumbnail of Bab II] Text (Bab II)
Bab II.pdf
Restricted to Registered users only

Download (486kB)
[thumbnail of Bab III] Text (Bab III)
Bab III.pdf
Restricted to Registered users only

Download (717kB)
[thumbnail of Bab IV] Text (Bab IV)
Bab IV.pdf
Restricted to Registered users only

Download (474kB)
[thumbnail of Bab V] Text (Bab V)
Bab V.pdf
Restricted to Registered users only

Download (51kB)
[thumbnail of Daftar Pustaka] Text (Daftar Pustaka)
Daftar Pustaka.pdf
Restricted to Registered users only

Download (122kB)
[thumbnail of Lampiran] Text (Lampiran)
Lampiran.pdf
Restricted to Registered users only

Download (2MB)
[thumbnail of Naskah Publikasi] Text (Naskah Publikasi)
Naskah Publikasi.pdf
Restricted to Registered users only

Download (515kB)
[thumbnail of Full Text] Text (Full Text)
Full Text.pdf
Restricted to Repository staff only

Download (4MB)

Abstract

METODE BLENDED MERUPAKAN SALAH SATU METODE UNTUK MEMPERBAIKI PRODUK YANG TELAH RUSAK ATAU TIDAK TERPAKAI SEHINGGA DAPAT DIGUNAKAN KEMBALI MENJADI PRODUK BARU. SALAH SATU PRODUK PLASTIK YANG MUDAH DIJUMPAI DAN BANYAK DIGUNAKAN ADALAH JENIS POLYPROPYLENE (PP). PP MERUPAKAN SALAH SATU POLIMER JENIS TERMOPLASTIK YANG DAPAT DIDAUR ULANG DAN PALING RINGAN DIANTARA BAHAN POLIMER LAINNYA. SECARA UMUM PEMBUATAN PRODUK PLASTIK DAPAT DILAKUKAN DENGAN MENGGUNAKAN MESIN INJECTION MOULDING DAN MESIN EKSTRUSI. NAMUN BIAYA PEMBUATAN PRODUK PLASTIK MENGGUNAKAN MESIN INJECTION MOLDING RELATIF MAHAL, OLEH KARENA ITU PENELITIAN PP MURNI DAN PP DAUR ULANG PADA PENELITIAN INI MENGGUNAKAN MESIN EKSTRUSI. PENELITIAN INI BERTUJUAN UNTUK MENGETAHUI PENGARUH BLENDING RATIO DAN MELTING TEMPERATURE TERHADAP UJI TARIK DAN STRUKTUR MORFOLOGI CAMPURAN PP MURNI DAN PP DAUR ULANG.

PENELITIAN DILAKUKAN DENGAN MEMBUAT SPESIMEN MULTIPURPOSE SESUAI DENGAN STANDAR ASTM D 638 DARI BAHAN MATERIAL BUTIRAN PP MURNI DAN PP DAUR ULANG. PROSES PENGOLAHAN CAMPURAN PP MURNI DAN PP DAUR ULANG DILAKUKAN DENGAN MENGGUNAKAN MESIN EKSTRUSI. METODE BLENDED DILAKUKAN DENGAN RATIO PP MURNI 70% : PP DAUR ULANG 30%, PP MURNI 80% : PP DAUR ULANG 20%, DAN PP MURNI 90% : PP DAUR ULANG 10%. PENGUJIAN SPESIMEN YANG DILAKUKAN YAITU PENGUJIAN TARIK DAN PENGUJIAN MIKRO.

HASIL PENGUJIAN TARIK MENUNJUKKAN MODULUS ELASTISITAS UNTUK PERBANDINGAN 90% PP MURNI : 10% PP DAUR ULANG PADA TEMPERATUR 190OC SEBESAR 348 MPA SEDANGKAN UNTUK PERBANDINGAN 70% PP MURNI : 30% PP DAUR ULANG PADA TEMPERATUR 188OC SEBESAR 190 MPA. HASIL PENGUJIAN MIKRO MENUNJUKAN BAHWA SPESIMEN DENGAN PERBANDINGAN 70% PP MURNI : 30% PP DAUR ULANG PADA TEMPERATUR 188OC MENUNJUKKAN ADANYA DEGRADASI YANG CUKUP BANYAK. SEMAKIN BANYAK KANDUNGAN PP DAUR ULANG MAKA SEMAKIN TINGGI PELUANG MENGALAMI DEGRADASI, AKIBATNYA SPESIMEN MENJADI MUDAH RAPUH.

Item Type: Thesis (S1)
Uncontrolled Keywords: POLYPROPYLENE, BLENDED, PP DAUR ULANG, MELTING TEMPERATURE, BLENDING RATIO, EKSTRUSI, RECYCLED PP, EXTRUSION
Divisions: Fakultas Teknik > Teknik Mesin S1
Depositing User: Eko Kurnawan
Date Deposited: 09 Sep 2022 03:24
Last Modified: 09 Sep 2022 03:24
URI: https://etd.umy.ac.id/id/eprint/34220

Actions (login required)

View Item
View Item