MUJI BASUKI SANTOSO (2022) BETON RINGAN DENGAN AGREGAT LEMPUNG BAKAR DAN ADMIXTURE SUPERPLASTICIZER. S1 thesis, Universitas Muhammadiyah Yogyakarta.

	Text (Halaman Judul) Halaman Judul.pdf Download (692kB)
	Text (Lembar Pengesahan) Lembar Pengesahan.pdf Restricted to Registered users only Download (298kB)
	Text (Abstrak) Abstrak.pdf Restricted to Registered users only Download (11kB)
	Text (Bab I) Bab I.pdf Download (16kB)
	Text (Bab II) Bab II.pdf Restricted to Registered users only Download (602kB)
	Text (Bab III) Bab III.pdf Restricted to Registered users only Download (506kB)
	Text (Bab IV) Bab IV.pdf Restricted to Registered users only Download (106kB)
	Text (Bab V) Bab V.pdf Restricted to Registered users only Download (10kB)
	Text (Daftar Pustaka) Daftar Pustaka.pdf Restricted to Registered users only Download (75kB)
	Text (Lampiran) Lampiran.pdf Restricted to Registered users only Download (2MB)
	Text (Naskah Publikasi) Naskah Publikasi.pdf Restricted to Registered users only Download (239kB)
	Text (Full Text) Full Text.pdf Restricted to Repository staff only Download (4MB)

Abstract

MEMANFAATKAN LEMPUNG BAKAR SEBAGAI PENGGANTI AGREGAT KASAR MERUPAKAN SEBUAH INOVASI YANG BAIK DALAM DUNIA KONSTRUKSI. HAL INI KARENA BIASANYA ADA PERMASALAHAN DALAM HAL PENGADAAN AGREGAT KASAR PADA SEBUAH PROYEK KONSTRUKSI. KARENA ADA DAERAH YANG DIMANA SUMBER MATERIALNYA TERBATAS PADA BEBERAPA MATERIAL SAJA. LEMPUNG BAKAR MERUPAKAN SALAH SATU MATERIAL YANG RINGAN SEHINGGA DAPAT MENGURANGI BERAT BETON YANG CUKUP BESAR. AGREGAT LEMPUNG BAKAR TERBUKTI MEMILIKI BERAT JENIS 0,6% LEBIH RINGAN DARIPADA AGREGAT KASAR KERIKIL YANG BIASA DIGUNAKAN DALAM CAMPURAN BETON. PENELITIAN INI MENITIK BERATKAN PADA KUAT TEKAN DAN KUAT TARIK BELAH BETON RINGAN YANG AGREGAT KASARNYA DIRUBAH DENGAN VARIAN LEMPUNG BAKAR DENGAN CAMPURAN SUPERPLASTICIZER. PERSENTASE YANG DIGUNAKAN UNTUK CAMPURAN SUPERPLASTICIZER ADALAH 1%; 1,5%; 2%; DAN 2,5 PERSEN DIMANA BENDA UJI YANG DIGUNAKAN BERBENTUK SILINDER DENGAN DIMENSI TINGGI 15 CM DAN DIAMETER 7,5 CM. DARI HASIL PEGUJIAN DIDAPATKAN KUAT TEKAN RATA-RATA UNTUK BENDA UJI DENGAN VARIASI CAMPURAN SP 1% SEBESAR 6,53 MPA, SP 1,5% SEBESAR 6,56 MPA, SP 2% SEBESAR 6,65 MPA, SP 2,5% SEBESAR 8,06 MPA. NILAI KUAT TEKAN TERTINGGI DIPEROLEH OLEH BENDA UJI YANG MENGGUNAKAN VARIASI SUPERPLASTICIZER DENGAN PESENTASE 2,5% YAKNI DENGAN KUAT TEKAN RATA-RATA SEBESAR 8,06 MPA. NILAI KUAT TEKAN CENDERUNG MENINGKAT SEIRING DENGAN MENINGKATNYA PERSENTASE BAHAN TAMBAH YAKNI SUPERPLASTICIZER. UNTUK KUAT TARIK BELAH RATA-RATA DIDAPATKAN BENDA UJI DENGAN VARIASI CAMPURAN SP 1% SEBESAR 1,41 MPA, SP 1,5% SEBESAR 0,83 MPA, SP 2% SEBESAR 0,87 MPA, SP 2,5% SEBESAR 1,13 MPA. NILAI KUAT TARIK BELAH TERTINGGI DIPEROLEH OLEH BENDA UJI YANG MENGGUNAKAN VARIASI SUPERPLASTICIZER DENGAN PESENTASE 1% YAKNI DENGAN KUAT TARIK BELAH RATA-RATA SEBESAR 1,41 MPA. NILAI KUAT TARIK BELAH CENDERUNG MENINGKAT SEIRING DENGAN PENAMBAHAN PERSENTASE BAHAN TAMBAH YAKNI SUPERPLASTICIZER. PENINGKATAN MAKSIMUM BERADA PADA TITIK OPTIMUM SETELAH ITU CENDERUNG TERJADI PENURUNAN.

Dosen Pembimbing:	AS'AT PUJIANTO, IR., M.T., IPM. | NIDN0514046601
Item Type:	Thesis (S1)
Uncontrolled Keywords:	LIGHTWEIGHT CONCRETE, BURNT CLAY AGGREGATE, SUPERPLASTICIZER, COMPRESSIVE STRENGTH, SPLIT TENSILE STRENGTH
Divisions:	Fakultas Teknik > S1 Teknik Sipil
Depositing User:	M. Erdiansyah
Date Deposited:	14 Nov 2024 06:50
Last Modified:	14 Nov 2024 06:50
URI:	https://etd.umy.ac.id/id/eprint/35404

Actions (login required)

View Item