HILMY ROMADHON (2022) UJI DAKTILITAS DAN MODULUS ELASTIS MORTAR DENGAN CAMPURAN SERBUK KARET BAN BEKAS 0%, DAN 40%, USIA 7, 28, 56 HARI. S1 thesis, Universitas Muhammadiyah Yogyakarta.
Halaman Judul.pdf
Download (3MB)
Lembar Pengesahan.pdf
Restricted to Registered users only
Download (220kB)
Abstrak.pdf
Restricted to Registered users only
Download (497kB)
Bab I.pdf
Download (841kB)
Bab II.pdf
Restricted to Registered users only
Download (5MB)
Bab III.pdf
Restricted to Registered users only
Download (3MB)
Bab IV.pdf
Restricted to Registered users only
Download (2MB)
Bab V.pdf
Restricted to Registered users only
Download (294kB)
Daftar Pustaka.pdf
Restricted to Registered users only
Download (895kB)
Lampiran.pdf
Restricted to Registered users only
Download (4MB)
Naskah Publikasi.pdf
Restricted to Registered users only
Download (758kB)
Full Text.pdf
Restricted to Repository staff only
Download (23MB)
Abstract
PEMBANGUNAN KONSTRUKSI BERKEMBANG SANGAT PESAT DI INDONESIA, SALAH SATU DIANTARANYA YAITU PADA TEKNOLOGI MORTAR YANG DITUNTUT SEMAKIN INOVATIF. KARET BAN BEKAS MERUPAKAN SALAH SATU JENIS LIMBAH YANG JUMLAHNYA SANGAT MELIMPAH. PEMANFAATAN LIMBAH KARET BAN BEKAS DI INDONESIA MASIH SANGAT TERBATAS. SALAH SATU PEMANFAATAN LIMBAH BAN BEKAS ADALAH MENCAMPURKAN SEBAGIAN AGREGAT HALUS DALAM CAMPURAN MORTAR. PENELITIAN INI MENGGUNAKAN AGREGAT HALUS DENGAN CAMPURAN SERBUK KARET BAN BEKAS SEBESAR 40%. PENELITIAN INI BERTUJUAN UNTUK MENGETAHUI PENGARUH PENAMBAHAN SERBUK KARET BAN BEKAS TERHADAP KUAT TEKAN SESUAI DENGAN USIA MORTAR. BENDA UJI BERUPA 18 BUAH BERBENTUK SILINDER DENGAN UKURAN DIAMETER 15 CM DAN TINGGI 30 CM, YANG TERDIRI DARI 9 BUAH MORTAR SKBB DAN 9 BUAH MORTAR NORMAL. SERBUK KARET BAN BEKAS DISARING MENGGUNAKAN SARINGAN NO.4 YANG KEMUDIAN DICAMPURKAN DALAM MORTAR SEBAGAI PENGGANTI SEBAGIAN AGREGAT HALUS. PENGUJIAN DALAM PENELITIAN INI BERUPA DAKTILITAS, MODULUS ELASTISITAS, DAN KUAT TEKAN MORTAR. UMUR MORTAR YANG DIUJI PADA PENELITIAN INI YAITU PADA SAAT MORTAR BERUMUR 7, 28, DAN 56 HARI. HASIL PENELITIAN MENUNJUKAN BAHWA MORTAR SKBB MERUPAKAN MORTAR DENGAN RATA-RATA KUAT TEKAN SEBESAR 2,71 MPA, 3,4 MPA, DAN 4,09 MPA, DAKTILITAS SEBESAR 2,04, 1,69, DAN 1,56, DAN MODULUS ELASTISITAS SEBESAR 273,72, 398,583, DAN 508,303. PENAMBAHAN SKBB PADA CAMPURAN MORTAR DAPAT MENURUNKAN KUAT TEKAN, MODULUS ELASTISITAS, AKAN TETAPI DAPAT MENINGKATKAN DAKTILITAS MORTAR, TETAPI SEIRING BERTAMBAHNYA USIA MORTAR KUAT TEKAN, MODULUS ELASTISITAS MENGALAMI PENINGKATAN, DAN DAKTILITAS MENGALAMI PENURUNAN.
Item Type: | Thesis (S1) |
---|---|
Uncontrolled Keywords: | MORTAR, TIRE RUBBER POWDER, COMPRESSIVE STRENGTH, DUCTILITY, MODULUS OF ELASTICITY |
Divisions: | Fakultas Teknik > Teknik Sipil S1 |
Depositing User: | M. Erdiansyah |
Date Deposited: | 22 Nov 2023 03:32 |
Last Modified: | 22 Nov 2023 03:32 |
URI: | https://etd.umy.ac.id/id/eprint/35455 |