RIZQI ALDI PRATAMA (2022) UJI DAKTILITAS DAN MODULUS ELASTIS MORTAR DENGAN CAMPURAN SERBUK KARET BAN BEKAS 0% DAN 30% USIA 7, 28, 56 HARI. S1 thesis, Universitas Muhammadiyah Yogyakarta.
Halaman Judul.pdf
Download (961kB)
Lembar Pengesahan.pdf
Restricted to Registered users only
Download (168kB)
Abstrak.pdf
Restricted to Registered users only
Download (339kB)
Bab I.pdf
Download (418kB)
Bab II.pdf
Restricted to Registered users only
Download (907kB)
Bab III.pdf
Restricted to Registered users only
Download (1MB)
Bab IV.pdf
Restricted to Registered users only
Download (676kB)
Bab V.pdf
Restricted to Registered users only
Download (326kB)
Daftar Pustaka.pdf
Restricted to Registered users only
Download (340kB)
Lampiran.pdf
Restricted to Registered users only
Download (5MB)
Naskah Publikasi.pdf
Restricted to Registered users only
Download (586kB)
Full Text.pdf
Restricted to Repository staff only
Download (28MB)
Abstract
PENGGUNAAN BAHAN MATERIAL KONSTRUKSI KHUSUSNYA DI INDONESIA MASIH BANYAK MENGGUNAKAN MATERIAL YANG BERASAL DARI ALAM, YANG KETERSEDIAANNYA SEWAKTU-WAKTU DAPAT HABIS. UNTUK MENGATASI HAL TERSEBUT PERLU DILAKUKAN INOVASI SALAH SATUNYA YAITU DENGAN MEMANFAATKAN LIMBAH YANG ADA SEBAGAI BAHAN PENGGANTI MATERIAL YANG BERASAL DARI ALAM. PEMANFAATAN LIMBAH JUGA DAPAT SEKALIGUS MENGURANGI PENCEMARAN LINGKUNGAN. LIMBAH BAN MERUPAKAN SALAH SATU LIMBAH YANG MASIH SEDIKIT PEMANFAATANNYA, PADAHAL JUMLAHNYA SANGAT MELIMPAH DAN LIMBAH INI SULIT TERURAI. PADA PENELITIAN INI DILAKUKAN PENGUJIAN DAKTILITAS DAN MODULUS ELASTIS MORTAR DENGAN CAMPURAN SERBUK KARET BAN BEKAS (SKBB) DENGAN PERSENTASE 0 PERSEN DAN 30 PERSEN, SERTA USIA PENGUJIAN 7, 28 DAN 56 HARI. BENDA UJI BERBENTUK SILINDER DENGAN DIAMETER 15 CM DAN TINGGI 30 CM. JUMLAH TOTAL BENDA UJI YAITU 18 BUAH MORTAR YANG TERDIRI DARI 6 BUAH MORTAR TIAP USIA PENGUJIANNYA. AGREGAT HALUS BERUPA PASIR YANG DIGUNAKAN DISARING TERLEBIH DAHULU MENGGUNAKAN SARINGAN NO.4 (4,75 CM), YANG DICAMPURKAN DENGAN SERBUK KARET BAN BEKAS SEBANYAK 30 PERSEN YANG SEBELUMNYA DISARING MENGGUNAKAN SARINGAN YANG SAMA. DARI HASIL PENGUJIAN YANG DILAKUKAN MENUNJUKAN BAHWA DENGAN PENAMBAHAN SERBUK KARET BAN BEKAS MENYEBABKAN PENURUNAN NILAI KUAT TEKAN DAN JUGA NILAI MODULUS ELASTIS MORTAR, NAMUN DAPAT MENINGKATKAN NILAI DAKTILITASNYA. NILAI KUAT TEKAN TERTINGGI YAITU MORTAR SKBB 0 PERSEN SEBESAR 14,747 MPA DI USIA 56 HARI, KEMUDIAN NILAI MODULUS ELASTIS TERTINGGI YAITU PADA MORTAR SKBB 0 PERSENSEBESAR 1446,67 MPA PADA USIA 56 HARI, DAN NILAI DAKTILITAS TERTINGGI YAITU PADA MORTAR SKBB 30 PERSEN SEBESAR 1,60 DI USIA 7 HARI.
Item Type: | Thesis (S1) |
---|---|
Uncontrolled Keywords: | mortar, used tire rubber powder, compressive strength, ductility, elastic modulus |
Divisions: | Fakultas Teknik > Teknik Sipil S1 |
Depositing User: | M. Erdiansyah |
Date Deposited: | 15 Dec 2023 08:32 |
Last Modified: | 15 Dec 2023 08:32 |
URI: | https://etd.umy.ac.id/id/eprint/35465 |