PROPERTI MEKANIK DAN METODE PENCEGAHAN KOROSI PADA SEA WATER MIXED MORTAR DENGAN LIMBAH BATCHING PLAN SEBAGAI PENGGANTI 50% AGREGAT HALUS

KOMPONEN PENYUSUN MORTAR HARUS DIRANCANG DENGAN BAIK AGAR MENGHASILKAN KUALITAS PRODUK KONSTRUKSI YANG OPTIMAL. PENGGUNAAN LIMBAH SISA BATCHING PLAN MENJADI SALAH SATU UPAYA MEMANFAATKAN DAN MENELITI PENGARUHNYA TERHADAP MATERIAL YANG DIGUNAKAN DALAM PENELITIAN INI. TUJUAN DARI PENELITIAN INI UNTUK MENGANALISA HASIL POTENSI KOROSI YANG DIPEROLEH DARI SPESIMEN MORTAR KUBUS DEGAN MATERIAL PENGGANTI AGREGAT HALUS 50% MENGGUNAKAN LIMBAH BATCHING PLANT YANG DITERAPKAN COATING PADA TULANGAN DAN COATING PADA PERMUKAAN MORTAR DENGAN MENGGUNAKAN PENGUJIAN HALF-CELL POTENTIAL. PENELITIAN INI JUGA MENGANALISA DENSITAS SPESIMEN SILINDER MORTAR, HASIL KUAT LENTUR DARI PENGUJIAN FLEXURAL TEST PADA MORTAR BALOK, MENGANALISA KUAT TARIK BELAH SILINDER MORTAR DENGAN PENGUJIAN SPLIT TENSILE STRENGTH, DAN KUAT TEKAN YANG DIPEROLEH DARI PENGUJIAN COMPRESSIVE STRENGTH TEST SILINDER MORTAR. HASIL PENELITIAN INI MENUNJUKAN POTENSI KOROSI YANG DIPEROLEH PADA TULANGAN SPESIMEN KUBUS DENGAN KETEBALAN SELIMUT 3 CM LEBIH TINGGI DARIPADA NILAI POTENSI KOROSI PADA TULANGAN TEBAL SELIMUT 10 CM, HASIL COATING PALING EFEKTIF MELINDUNGI TERHADAP KOROSI TERJADI PADA METODE STEEL COATING, NILAI DENSITAS SILINDER RATA-RATA 2,16 GR/CM3, HASIL KUAT TARIK BELAH SILINDER RATA-RATA 1,51 MPA, HASIL KUAT TEKAN SILINDER RATA-RATA SEBESAR 10,99 MPA, HASIL KUAT LENTUR BALOK RATA-RATA SEBESAR 2,85 MPA.